Esab OK67.60 E309L 3.2mm electrode welding rods 1.8KG PACK

46PiecesPer Pack

Acid-rutile coated MMA-electrode giving an overalloyed weld metal. Suitable for welding stainless steel to mild and low alloyed steels. Also suitable for welding of transition layers when surfacing mild steel with stainless steel weld metal.

Classifications EN ISO 3581-A : E 23 12 L R 3 2
SFA/AWS A5.4 : E309L-17
CSA W48 : E309L-17
Werkstoffnummer : 1.4332 Approvals CE : EN 13479
CWB : E309L-17
DNV-GL : VL 309
NAKS/HAKC : 2.5-4.0 mm
Seproz : UNA 272580
VdTV : 00898

Approvals are based on factory location. Please contact ESAB for more information.

Alloy Type Austenitic CrNi Coating Type Acid Rutile Ferrite Content FN 10-22 Welding Current DC+, AC Tensile_Properties Testing Condition Yield Strength Tensile Strength Elongation ISO As Welded 470 MPa ( 68 ksi ) 580 MPa ( 84 ksi ) 32 % Charpy Testing Testing Condition Testing Temp Impact Value ISO As Welded 20 C ( 68 F ) 50 J ( 37 ft-lb ) As Welded -10 C ( 14 F ) 40 J ( 30 ft-lb ) Analysis C Si Mn Cr Ni N Ferrite FN Typical Weld Metal Analysis % 0.03 0.8 0.9 23.7 12.4 0.09 15 Deposition Data Deposition rate at 90Per Diameter Efficiency (Per) Amps Volts Fusion time per electrode at 90Per I max Number of electrodes/kg weld metal 0.7 kg/h
( 1.5 lbs/h ) 2.0 x 300.0 mm
( 5/64 x 11.8 in. ) 60 % 45-65 A 27 V 38 sec 136 1.1 kg/h
( 2.4 lbs/h ) 2.5 x 300.0 mm
( 0.098 x 11.8 in. ) 60 % 45-90 A 28 V 38 sec 85 1.6 kg/h
( 3.5 lbs/h ) 3.2 x 350.0 mm
( 1/8 x 13.8 in. ) 60 % 65-120 A 29 V 51 sec 45 2.5 kg/h
( 5.5 lbs/h ) 4.0 x 350.0 mm
( 5/32 x 13.8 in. ) 60 % 85-180 A 31 V 51 sec 29 3.3 kg/h
( 7.3 lbs/h ) 5.0 x 350.0 mm
( 0.197 x 13.8 in. ) 60 % 110-250 A 32 V 58 sec 19